Mix used for creating micro-pebble & polished terrazzo coverings
Suitable for applications indoors and outdoors and special constructions
Indicative mixture of the PLANOCOLOR TERRAZZO system for applications on floors, walls and horizontal surfaces. It consists of PLANOCOLOR GRANULATES and the hydraulic binder NOVACEM CREATIVE. The components of the mix are packaged separately. The mixture is suitable for:
• creating:
o textured, non-slip surfaces with natural look or appearance
o polished terrazzo surfaces
o furniture, tables, offices, benches
• applications on horizontal and vertical surfaces in areas such as:
o external floors, terraces, balconies, water structures such as fountains, swimming pools, etc
o internal floors, bathrooms and wet areas
o heavy traffic floors, showrooms, commercial centers, public buildings or offices
o surfaces with underfloor heating systems
• application on various substrates such as:
o concrete or screeds
o existing coverings such as tiles, natural stones
o mortars and masonry mortars
o cement boards and gypsum boards (after a suitable primer application, provided that the surface is stable)
Refer to the Technical Data Sheets and Safety Data Sheets of the products listed here before the final selection of the mix for each application.
• Form: Powder
• Color: See photo
• Chemical substance: Mixture of Portland cement aggregates, polymers and special additives
• Specific gravity of the mix: 2,1 ± 0,1 kg/L
• Dry density of the mix: 2,0 ± 0,1 kg/L
• Workability: ≈ 60 – 90 min / 20°C
• Walkability: 2 – 3 hours/ 20 – 23°C and 60 – 65% RH
• Application temperature: from +5°C up to +35°C
195 OXIDE formulation consists of a dry mix as follows:
INGREDIENT DRY MIX RATIO
NOVACEM CREATIVE 35,0%
PLANOCOLOR GRANULATES RC GLASS GREEN MIX 30 15,0%
PLANOCOLOR GRANULATES RC GLASS GREEN MIX 70 50,0%
NOVACOLOR OXIDE BLUE 1 pc 250 gr
NOVACEM CREATIVE 35%*
Recommended water quantity 15 – 18%
Final performance with 16,5% water / mix ratio
Compressing strength 8 h ≥ 8 N/mm² ΕΝ 13892-2
1 d ≥ 18 N/mm²
7 d ≥ 41 N/mm²
28 d ≥ 47 N/mm²
Flexural strength 8 h ≥ 2 N/mm² ΕΝ 13892-2
1 d ≥ 3 N/mm²
7 d ≥ 5 N/mm²
28 d ≥ 6 N/mm²
Adhesion ≥ 2,4 N/mm² ΕΝ 13892-8
Chloride ion content ≤ 0,03% ΕΝ 1015-17
Capillary water absorption ≤ 0,04 kg/m² √h EN 1015-18
Water vapour permeability coefficient μ ≤ 20 EN 1015-19
Adhesion after weathering cycles ≥ 2,3 N/mm² EN 1015-21
Thermal conductivity mean λ10, dry, mat - values (W/m·K) 1,11 W/mK EN 1745
Capillary absorption ≤ 0,01 g/mm² EN 480-5
Capillary absorption ≤ 0,22 kg/m² √h EN 13057
Chloride ion ingress 0,01% EN 13396
Thermal compatibility part 1: ≥ 2,2 N/mm² EN 13687-1
Wear resistance A9 EN 13892-3
Reaction to fire A1 EN 13501-1
*Received data with the addition of PLANOCOLOR GRANULATES of the above 195 OXIDE mix formulation at 20°C - 23°C temperature and 60 – 65% R.H. without aeration. The Technical Data provided are the result of laboratory measurements in controlled conditions using the hydraulic binder NOVACEM CREATIVE, PLANOCOLOR GRANULATES as well as specific amount of mixing water. The use of different granulates or the addition of larger amount of mixing water due to specific conditions at the building site may reduce the final performance.
• Form: Powder
• Color: See photo
• Chemical substance: Mixture of Portland cement aggregates, polymers and special additives
• Specific gravity of the mix: 2,1 ± 0,1 kg/L
• Dry density of the mix: 2,0 ± 0,1 kg/L
• Workability: ≈ 60 – 90 min / 20°C
• Walkability: 2 – 3 hours/ 20 – 23°C and 60 – 65% RH
• Application temperature: from +5°C up to +35°C
195 OXIDE formulation consists of a dry mix as follows:
INGREDIENT DRY MIX RATIO
NOVACEM CREATIVE 35,0%
PLANOCOLOR GRANULATES RC GLASS GREEN MIX 30 15,0%
PLANOCOLOR GRANULATES RC GLASS GREEN MIX 70 50,0%
NOVACOLOR OXIDE BLUE 1 pc 250 gr
NOVACEM CREATIVE 35%*
Recommended water quantity 15 – 18%
Final performance with 16,5% water / mix ratio
Compressing strength 8 h ≥ 8 N/mm² ΕΝ 13892-2
1 d ≥ 18 N/mm²
7 d ≥ 41 N/mm²
28 d ≥ 47 N/mm²
Flexural strength 8 h ≥ 2 N/mm² ΕΝ 13892-2
1 d ≥ 3 N/mm²
7 d ≥ 5 N/mm²
28 d ≥ 6 N/mm²
Adhesion ≥ 2,4 N/mm² ΕΝ 13892-8
Chloride ion content ≤ 0,03% ΕΝ 1015-17
Capillary water absorption ≤ 0,04 kg/m² √h EN 1015-18
Water vapour permeability coefficient μ ≤ 20 EN 1015-19
Adhesion after weathering cycles ≥ 2,3 N/mm² EN 1015-21
Thermal conductivity mean λ10, dry, mat - values (W/m·K) 1,11 W/mK EN 1745
Capillary absorption ≤ 0,01 g/mm² EN 480-5
Capillary absorption ≤ 0,22 kg/m² √h EN 13057
Chloride ion ingress 0,01% EN 13396
Thermal compatibility part 1: ≥ 2,2 N/mm² EN 13687-1
Wear resistance A9 EN 13892-3
Reaction to fire A1 EN 13501-1
*Received data with the addition of PLANOCOLOR GRANULATES of the above 195 OXIDE mix formulation at 20°C - 23°C temperature and 60 – 65% R.H. without aeration. The Technical Data provided are the result of laboratory measurements in controlled conditions using the hydraulic binder NOVACEM CREATIVE, PLANOCOLOR GRANULATES as well as specific amount of mixing water. The use of different granulates or the addition of larger amount of mixing water due to specific conditions at the building site may reduce the final performance.
Back